| 6000 CERAMIC NON-STICK COATINGS |
¡ª Instruction
Waipolon 6000 system is a kind of nano-inorganic ceramic coating. The main ingredient is nano-inorganic compounds, which is completely inorganic molecular structure with a natural non-toxic property after the film formed. The coatings have many advantages£¬such as high hardness, high wear-resistant, high temperature resistance, weather resistance, re-rot resistance, etc. After curing the coating, the surface of the coating looks smooth£¬and the coating film is similar to the ceramic material.
¡ª Application
Cast aluminum heating plate, electric iron soleplate, perming device, knives, etc.
¡ª Specification
| No. |
Item |
Specification |
| 1 |
Color |
Adjustable |
| 2 |
Glossiness |
Adjustable |
| 3 |
Viscosity |
10¡À2¡å/ 25¡æ, NK-2 cup |
| 4 |
Solid content |
35¡À5% |
| 5 |
Density |
1.15 ~1.42 g / cm3 |
| 6 |
Thickness |
20¡À5µm |
| 7 |
Storage stability |
5~15¡æ¡Á1 Mth |
| 8 |
Base material |
Cast aluminum, iron and alloys etc. |
| 9 |
Preprocessing |
Degreasing and abrasive blasting (80 mesh) |
| 10 |
Application method |
Automatic air spray or manual application |
| 11 |
Spreading area |
8-10©O/kg |
| 12 |
Applicable viscosity |
12¡À2¡å, NK-2 cup |
| 13 |
Curing condition |
1C1B£º10 min / 240¡æ£»2C1B£º5min / 60¡æ + 10 min /240¡æ |
| 14 |
Packing |
5 kg / drum or 10 kg / drum or 20 kg/ drum |
¡ª Standards for non-stick aluminum pan, oven, rice cooker and other non-stick, heat resistant, wear-resistant cooking system
| No. |
Test Item |
Test Condition |
Request |
| 1 |
Cold pencil Hardness |
Mitsubishi pencil |
7~8 H |
| 2 |
Thermal pencil hardness (300¡æ) |
Mitsubishi pencil |
¡Ü6H |
| 3 |
Adhesion |
Grid adhesion£¨1.5mm¡Á1.5mm£© |
100 /100 |
| 4 |
MEK solvent resistance |
200 double rubs |
No change |
| 5 |
Acid resistance |
5% sulfuric acid, 48 Hours |
No change |
| 6 |
Non-sticking |
Fry more than 6 Eggs |
Pour available No scratch |
| 7 |
Abrasion |
1.5 kg scourers rub 2500 times |
No peeling |
| 8 |
Salt water resistance |
Start from the salt water boiling,20 min per time for 3 cycles |
No change No peeling |
| 9 |
Alkali resistance |
5% NaHCO3,48Hours |
No change |
| 10 |
Heat resistance |
500¡æ¡Á 1Hour |
No change |
| 11 |
Quickly heating and cooling |
After 350¡æ¡Á 0.5 Hour then put in the cold water for 4 cycles |
No blistering No change |
| 12 |
Boil water |
Continuous boiling for 4 Hours,Then draw grid |
No blistering No peeling |
| 13 |
Cooking |
More than 500 times |
Easy cleaning No peeling |
¡ª Caution
Agitate the coating fully before use (1 Hour is preferable). The above data is based on the test result of our laboratory, only for reference. Please test all the properties before using this product. Make appropriate adjustments according to the processing equipments. |
|